| Product Name | Ruimeifu PA6 MF200 |
| Base Resin | Polyamide 6 (Nylon 6) |
| Filler Content | Mineral filled |
| Filler Percentage | 20% |
| Color | Natural |
| Density | 1.35 g/cm³ |
| Melt Flow Index | 18 g/10min (230°C/2.16kg) |
| Tensile Strength | 70 MPa |
| Elongation At Break | 3% |
| Flexural Modulus | 3200 MPa |
| Moisture Absorption | 1.2% |
| Heat Deflection Temperature | 160°C |
| Flame Retardancy | None |
| Processing Method | Injection molding |
As an accredited Ruimeifu PA6 MF200 factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
| Packing | The Ruimeifu PA6 MF200 is packaged in a 25 kg white woven bag, labeled with product name, specifications, and manufacturer. |
| Storage | Ruimeifu PA6 MF200 should be stored in a cool, dry, and well-ventilated area, away from direct sunlight and sources of heat or ignition. Keep the packaging tightly sealed to prevent moisture absorption and contamination. Avoid contact with strong acids, bases, and oxidizing agents. Proper storage ensures the material’s quality and extends its shelf life. |
| Shipping | Ruimeifu PA6 MF200 is securely packaged in moisture-resistant, industrial-grade bags or containers, each labeled for clear identification. During shipping, it is transported on pallets to prevent damage, ensuring protection from sunlight, moisture, and contamination. Handling complies with standard safety regulations for engineering plastics to maintain product integrity. |
Competitive Ruimeifu PA6 MF200 prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please call us at +8615651039172 or mail to sales9@boxa-chemical.com.
We will respond to you as soon as possible.
Tel: +8615651039172
Email: sales9@boxa-chemical.com
West Ujimqin Banner, Xilingol League, Inner Mongolia, China